Knife Thread
i was planing on placing it in the furnace just after my dad has finished using it so it will be at 1000c, then just leave it in there while the furnace cools
will that work well for softening the file? ill worry about the rest of the proces once the blade is shaped
sorry i have no experience in any of this so any additional information would be much appreciated.
will that work well for softening the file? ill worry about the rest of the proces once the blade is shaped
sorry i have no experience in any of this so any additional information would be much appreciated.
why make it if it dosent shoot?
- jackssmirkingrevenge
- Five Star General
- Posts: 26203
- Joined: Thu Mar 15, 2007 11:28 pm
- Has thanked: 569 times
- Been thanked: 343 times
- pneumaticcannons
- Specialist 3
- Posts: 392
- Joined: Sat Oct 30, 2010 9:45 am
- Location: shite country in asia
- Contact:
- jackssmirkingrevenge
- Five Star General
- Posts: 26203
- Joined: Thu Mar 15, 2007 11:28 pm
- Has thanked: 569 times
- Been thanked: 343 times
In theory it would work with both, but using the spring might scratch the inside of the knife handle and compromise sealing.pneumaticcannons wrote:Does jake plan on making it interchangeable with the spring?
hectmarr wrote:You have to make many weapons, because this field is long and short life
- jakethebeast
- Corporal 5
- Posts: 945
- Joined: Sat Jul 03, 2010 4:20 pm
- Location: Jakes cave
Im thinking of keeping this pure pneumatic, the fun part is that its steel, so it can take ALOT of pressure
Its little rough, some spot welding and sanding will do miracles
Its little rough, some spot welding and sanding will do miracles
Est Sularus Oth Mithas
- pneumaticcannons
- Specialist 3
- Posts: 392
- Joined: Sat Oct 30, 2010 9:45 am
- Location: shite country in asia
- Contact:
Look's great
What type of blade are you planning on using?..... Please don't make it black ops style
What type of blade are you planning on using?..... Please don't make it black ops style
Oh, I just assumed because you said convertIn theory it would work with both, but using the spring might scratch the inside of the knife handle and compromise sealing.
ramicaza <- My Youtube Channel
- jakethebeast
- Corporal 5
- Posts: 945
- Joined: Sat Jul 03, 2010 4:20 pm
- Location: Jakes cave
I havent even played Blck Ops I was thinking a 25cm long dagger blade, long and thin
Est Sularus Oth Mithas
- Fnord
- First Sergeant 2
- Posts: 2239
- Joined: Tue Feb 13, 2007 9:20 pm
- Location: Pripyat
- Been thanked: 1 time
- Contact:
Hey jake, just saw this on 4HV, you need one of these
http://4hv.org/e107_plugins/forum/forum ... php?129196
http://4hv.org/e107_plugins/forum/forum ... php?129196
- jakethebeast
- Corporal 5
- Posts: 945
- Joined: Sat Jul 03, 2010 4:20 pm
- Location: Jakes cave
Why? uses heck alot of electricity, whitch is getting more and more expensive , gas and coal is much more cheaper way
Est Sularus Oth Mithas
- pneumaticcannons
- Specialist 3
- Posts: 392
- Joined: Sat Oct 30, 2010 9:45 am
- Location: shite country in asia
- Contact:
- jakethebeast
- Corporal 5
- Posts: 945
- Joined: Sat Jul 03, 2010 4:20 pm
- Location: Jakes cave
Im more to Medal of Honors, Battlefields, older Call of Dutys, and the Elder scrolls, playing Skyrim as we speak
Est Sularus Oth Mithas
- jakethebeast
- Corporal 5
- Posts: 945
- Joined: Sat Jul 03, 2010 4:20 pm
- Location: Jakes cave
And got time to finish this puukko!
Handle in this one is made from walnut, brass and reindeershide
Blade is silversteel, around 59hrc, and razor sharp as always
Shieth is made from 3.5mm bullhide, and has an insert made from birch
Handle in this one is made from walnut, brass and reindeershide
Blade is silversteel, around 59hrc, and razor sharp as always
Shieth is made from 3.5mm bullhide, and has an insert made from birch
Est Sularus Oth Mithas
- jackssmirkingrevenge
- Five Star General
- Posts: 26203
- Joined: Thu Mar 15, 2007 11:28 pm
- Has thanked: 569 times
- Been thanked: 343 times
- Labtecpower
- Sergeant 3
- Posts: 1297
- Joined: Sat Feb 20, 2010 6:38 am
- Location: Pyongyang
- Has thanked: 5 times
- Been thanked: 13 times
very sexy!
If I got one I would play with it all day long
Teachers are getting used to it now
If I got one I would play with it all day long
Teachers are getting used to it now
- jakethebeast
- Corporal 5
- Posts: 945
- Joined: Sat Jul 03, 2010 4:20 pm
- Location: Jakes cave
Glad you like it JSR And for the sharpness, it is 52100 ballbearing steel, hardened to a whopping 67hrc. I literally shaved aluminium with it
Lab, tell me if ya want one
EDIT: and yeah, after shaving aluminium i didn't even resharpen it
Lab, tell me if ya want one
EDIT: and yeah, after shaving aluminium i didn't even resharpen it
Est Sularus Oth Mithas